Leictreoid grafite UHP 500mm
| Sonraíocht Theicniúil Comparáide le haghaidh Leictreoid Ghraifíte UHP 20" | ||
| Leictreoid | ||
| Mír | Aonad | Sonraíocht Soláthraí |
| Tréithe tipiciúla an Phoill | ||
| Trastomhas Ainmniúil | mm | 500 |
| Trastomhas uasta | mm | 511 |
| Trastomhas Íosta | mm | 505 |
| Fad Ainmniúil | mm | 1800-2400 |
| Fad Max | mm | 1900-2500 |
| Fad Min | mm | 1700-2300 |
| Dlús Bulc | g/cm3 | 1.68-1.72 |
| neart trasnach | MPa | ≥12.0 |
| Modal Óg | GPa | ≤13.0 |
| Friotaíocht Sonrach | µΩm | 4.5-5.6 |
| Uasdlús reatha | KA/cm2 | 18-27 |
| Acmhainn Iompraíochta Reatha | A | 38000-55000 |
| (CTE) | 10-6 ℃ | ≤1.2 |
| ábhar fuinseog | % | ≤0.2 |
| Tréithe tipiciúla Nipple (4TPI) | ||
| Dlús Bulc | g/cm3 | 1.78-1.84 |
| neart trasnach | MPa | ≥22.0 |
| Modal Óg | GPa | ≤18.0 |
| Friotaíocht Sonrach | µΩm | 3.4～ 3.8 |
| (CTE) | 10-6 ℃ | ≤1.0 |
| ábhar fuinseog | % | ≤0.2 |
Is é leictreoid graifít an t-aon ábhar atá in ann teocht ard suas le 3000 céim Celsius a sheasamh gan a bheith dífhoirmithe agus leáite. Mar sin, roghnaítear iad chun cruach a dhéanamh i bhfoirnéisí stua leictreach (EAF) agus foirnéisí ladle (LF).
Conas a oibríonn sé go praiticiúil? Agus sruth leictreach ag dul tríd an leictreoid, cruthaíonn na leideanna leictreoid stua leictreach a ghineann teas an-ard agus a leánn an cruach ina iarann leáite. Mar gheall ar fhriotaíocht teocht ard agus ar fhriotaíocht turrainge teirmeach is ábhar fíor-riachtanach é le haghaidh cruach a dhéanamh.